Yeah that makes perfect sense! What you were talking about with the S dies is why I started using the Lee collet, because I had heard that they don't cause much runout. I gave my process some more thought and realized that the body die should probably be my first step, rather than my second. So beyond overworking my cases, I'm probably also causing more problems there.
As far as annealing goes. What I found on 6mmBR.com wanted me to buy some annealing kit. Is there a way around this for a broke college kid? If I can chuck cases up in a drill,set up a propane torch with some tempilaq, and dump them in a bucket of water, would that work?
I appreciate all the info.